Peerless Industrial Group, as a manufacturer of chain, can only control the specifications of our chain products in accordance with industry and governmental standards for chain manufacturing. It would be impossible for any warning to contain all of the possible misapplications associated with the use of Peerless Industrial Group products. Our warnings are intended to identify only those risks which are most common. The responsibility and understanding of the proper safe use and application of the products in our catalog, ultimately rest with the end user.

We are not responsible for the end user’s assembly in which our chain may be used. Failure of the product can occur due to misapplication, abuse, intentional alteration or improper maintenance. Product failure can result in property damage, personal injury or death.

Working Load Limit (WLL)

The “Working Load Limit” (rated capacity) is the maximum load that shall be applied in direct tension to an undamaged straight length of chain.

Proof Test

The “Proof Test” (manufacturing test force) is a term designating the minimum tensile force which has been applied to a chain under constantly increasing force in direct tension during the manufacturing process. These loads are manufacturing integrity tests and shall not be used as criteria for service or design purposes.

Minimum Breaking Force

The “Minimum Breaking Force” is the minimum force at which the chain during manufacture has been found by testing to break when a constantly increasing force is applied in direct tension. Breaking force values are not guarantees that all chain segments will endure these loads. This test is a manufacturer’s attribute acceptance test and shall not be used as a criteria for service or design purposes.

The Working Load Limits and the associated safety factor of each Peerless product may be affected by wear, misuse, overloading, corrosion, deformation, intentional alteration and other use conditions. Regular inspection must be conducted to determine whether use can be continued at the assigned Working Load Limit, a reduced Working Load Limit or whether the product must be withdrawn from service. The terms “Working Load Limit”, “Proof Test” and “Minimum Breaking Force” contain no implication of what load the chain will withstand if the chain is used in such conditions of abuse and misuse. Peerless Industrial Group accepts no liability for any such abuse or misuse.

The Working Load Limit of a sling or assembly must not exceed the lowest Working Load Limit of the components in the sling or assembly. Use only Peerless Industrial Group approved parts as replacements when servicing or repairing original Peerless Industrial Group slings or assemblies.

USE ONLY GRADE 80 OR GRADE 100 ALLOY CHAIN AND ATTACHMENTS FOR OVERHEAD LIFTING. Please see page 6 for more information regarding alloy chain Working Load Limits in relation to the angle of lift.

PEERLESS INDUSTRIAL GROUP PRODUCTS ARE INTENDED TO BE USED AT OR BELOW THE MAXIMUM WORKING LOAD LIMITS SPECIFIED IN CONSTANTLY INCREASING FORCE APPLICATIONS UNDER DIRECT TENSION OR IN A STRAIGHT LINE PULL.

SHOCK LOADING IS PROHIBITED AND SIDE LOADING MUST BE AVOIDED, AS IT EXERTS ADDITIONAL DYNAMIC FORCES OR LOADING WHICH THE PRODUCT IS NOT DESIGNED TO ACCOMMODATE.

THE CONDITIONS INVOLVING USE IN CERTAIN ENVIRONMENTAL SITUATIONS SUCH AS UNUSUAL (HIGH OR LOW) TEMPERATURE, CHEMICAL, ETC…, CAN CAUSE CHANGES IN CHAIN PERFORMANCE.

All chains and attachments in this catalog are capable of creating sparks unless otherwise noted.

Welding Peerless Industrial Group load support parts or products can be hazardous. Knowledge of materials, heat treatment and welding procedures are necessary for proper welding.

CONSULT PEERLESS INDUSTRIAL GROUP FOR ADDITIONAL INFORMATION OR QUESTIONS REGARDING THE USE AND APPLICATION OF THE PRODUCTS COVERED IN THIS CATALOG.

 Back to Top

Temperature and Chain

Use of Grade 63 Chain Under Heat Conditions

Effect of Elevated Temperature on the Working Load Limit of Grade 63 Alloy Chain

Chains should not be used outside of the -40º F to 400º F (-40º C to 204º C) temperature range without consulting the chain manufacturer. The specific working load limit reductions for Grade 63 chains used at and after exposure to elevated temperatures have been established and are shown below.

Maximum
Temperature of

Chain
Reduction of
Working Load Limit While At Temperature
Reduction of Working Load Limit After Exposure to Temperature
Below 400º None None
400º None None
500º None None
600º 10% None
700º 20% None
800º 30% None
900º 40% None
1000º 50% 10%
Over 1000º * (see below) * (see below)

* OSHA 1910.184 requires all slings exposed to temperatures over 1000º F to be removed from service.

Use of Grade 80 Chain Under Heat Conditions

Effect of Elevated Temperature on the Working Load Limit of Grade 80 Alloy Chain

Chains should not be used outside of the -40º F to 400º F (-40º C to 204º C) temperature range without consulting the chain manufacturer. The specific working load limit reductions for Grade 80 chains used at and after exposure to elevated temperatures have been established and are shown below.

Maximum
Temperature
of

Chain
Reduction of
Working Load
Limit While At Temperature
Reduction of Working Load Limit After Exposure to Temperature
Below 400º None None
400º 10% None
500º 15% None
600º 20% 5%
700º 30% 10%
800º 40% 15%
900º 50% 20%
1000º 60% 25%
Over 1000º * (see below) * (see below)

* OSHA 1910.184 requires all slings exposed to temperatures over 1000º F to be removed from service.

Use of Grade 100 Chain Under Heat Conditions

Effect of Elevated Temperature on the Working Load Limit of Grade 100 Alloy Chain

Chains should not be used outside of the -40º F to 400º F (-40º C to 204º C) temperature range without consulting the chain manufacturer. The specific working load limit reductions for Grade 100 chains used at and after exposure to elevated temperatures have been established and are shown below.

Maximum Temperature of Chain Reduction of Working Load Limit While At Temperature Reduction of Working Load Limit After Exposure to Temperature
Below 400º None None
400º 15% None
500º 25% 5%
600º 30% 15%
700º 40% 20%
800º 50% 25%
900º 60% 30%
1000º 70% 35%
Over 1000º * (see below) * (see below)

* OSHA 1910.184 requires all slings exposed to temperatures over 1000º F to be removed from service.

 Back to Top

Latch GuidelinesGeneral Hook & Latch Guidelines

Important Safety Information – Read & Follow

  • Always inspect hook and latch before using.
  • Never use a latch that is distorted or bent.
  • Always make sure spring will force the latch against the tip of the hook.
  • Always make sure hook supports the load. Do not point load hooks–load should bear on the bowl of hook. The latch must never support the load. (See Figure 1 & 2).
  • Latches are intended to retain loose sling of devices under slack conditions.
  • Latches are not intended to be an anti-fouling device.

 Back to Top

 

Table of Wear

If chain is worn to less than the minimum allowable thickness (T), remove the chain from service.  Chain Wear Illustration
Specifications
Size of Chain Material Diameter Min Allowable Thickness (T)
Inches mm Grade 80 Grade 100 Grade 80 Grade 100
9/32” 7mm 0.274 0.279 0.239
3/8” 10mm 0.392 0.404 0.342
1/2” 13mm 0.510 0.529 0.443
5/8” 16mm 0.630 0.625 0.546
3/4” 20mm 0.781 0.687
7/8” 22mm 0.906 0.750
1” 26mm 1.032 0.887
1-1/4” 32mm 1.250 1.091

 Back to Top

Safety Checklist

Check #1 – Inspections  Visually examine the sling before each use. Look for stretched, gouged, bent or worn links and components, including hooks, with open throats, cracks or distortion, if damaged, remove from service. Check 1: Inspections
Check 1B: Inspections
   
Check #2 -Balance  Know the load — determine the weight, center of gravity, angle and lift and select the proper size of sling. Check 2: Balance
   
Check #3 – Overload  Never overload the sling — check the working load limit on the identification tag. Always consider the effect of Angle of Lift — the tension on each leg of the sling is increased as the angle of lift, from horizontal, decreases. Use the chart in the Peerless Industrial Group catalog or in the Peerless Chain Sling User’s Manual for this purpose. Check 3: Overload
   
Check #4 -Knots, Twists & Kinks  Make sure chain is not twisted, knotted or kinked before lifting load. Slings should not be shortened with knots, bolts or other make-shift devices. Check 4: Knots, twists & kinks
   
Check #5 – Sharp Edges  Protect chain with padding when lifting sharp edged loads. Check 5: Sharp edges
   
Check #6 – Abrupt Movement  Lift and lower loads smoothly. Do not jerk. Check 6: Abrupt Movement
   
Check #7 – High Temperatures  Do not expose alloy chain or sling to temperatures of 400°F or higher. Check 7: Temperatures
   
Check #8 – Chain Care  Store slings properly on an A-Frame and protect chain slings from corrosion during storage. Check 8: Chain Care